| Wire electrode for
Welding Unalloyed and Low-alloy Steels |
|
|
|
|
| Standards: |
EN 440 |
G 42 4 M G3
Si 1 |
|
DIN 8559
|
SG 2 CY 42
43 |
|
AWS/ASME
SFA-5.18 |
ER 70 S - 6
|
|
TS 5618
|
SG 2 CY 42
43 |
|
M.No.
|
1.5125
| |
|
| Application and Properties: |
|
Unalloyed wire electrode
for GMA (MAG) welding of general structural steels and
pipe steels using CO2 or mixed shielding gas. Preheating
is required, depending on the plate thickness and carbon
equivalent of the base metal. A thin and homogeneous
copper coating protects the wires from
rusting. |
|
| Materials:
|
| S185 |
St 33 |
| S235 - S355 |
St 37.0 - 52.0
|
| S235 - S355 |
St 37-2 - St 52-3
|
| P235 - P355 |
St 37.4 - St 52.4
|
| P235 |
St 35.8 |
| P265 |
St 45.8 |
| P235GH , P265GH
|
HI, HII |
| P295GH , P355GH
|
17 Mn 4 , 19 Mn 5
|
| E295, E335 |
St 50 , St 60*
|
| L210 - L360 |
StE210.7(TM) -
StE360.7(TM) |
| - |
StE255, StE 380
|
| S(P)275 - S(P)355
|
StE 285 - StE 355
|
| - |
GS-38, GS-52
|
| GP240R |
GS-45 |
| - |
A, B, D, E |
|
| *Preheat to 150-300˚C,
depending on the plate thickness |
|
|
|
|
|
|
|
| All-Weld
Metal Analysis (typical values in %) : |
| 0.08 |
0.8 |
1.45 |
<0.025 |
<0.025 |
|
|
| Mechanical
Properties of All-Weld Metal (single values are typical
values): |
|
|
| AW : As welded |
|
| Chemical
compositions and mechanical properties apply to
the use of shielding gas |
|
: EN
439 - C1 (100% CO2) | |
|
| Shielding gas
as to EN 439 |
: C1 (100% CO2),
M21, M22, M23, M24 | |
|
| Welding rod for
TIG-welding |
: A1002
| |
| Shielding gas
consumption |
: 12 l/min for Ø
0.8 mm, 15 l/min for Ø 1.2 mm
| |
|
| Packing
& Order Information : |
| 2012000 |
0.60 |
15 |
| 2012001 |
0.80 |
15 |
| 2012002 |
0.90 |
15 |
| 2012003 |
1.00 |
15 |
| 2012005 |
1.20 |
15 |
| 2012007 |
1.40 |
15 |
| 2012008 |
1.60 |
15 |
| 2012009 |
2.00 |
15 |
| 2012010 |
2.40 |
15 |
| 2012501 |
0.80 |
250 |
| 2012503 |
1.00 |
250 |
| 2012505 |
1.20 |
250 |
|
|
| Type of
Current/Polarity/Welding Positions : |
| You can click on
the figure to see its explanation... |
|
|
|