Covered electrode for Welding Stainless and Heat
Resisting Steels
|
| Rutile-Basic Covering |
|
|
|
| Standards: |
EN 1600 |
E 22 9 3 LR
12 |
|
DIN 8556
|
E 22 9 3 LR
26 |
|
AWS/ASME
SFA-5.4 |
E 2209 - 16
|
|
M.No.
|
1.4462
| |
|
| Application and Properties: |
|
Electrode for welding
dublex (ferritic-austenitic) stainless Cr-Ni-Mo steels.
Suitable also for welding dublex stainless steels to
carbon steels. The delta-ferrite content of the
as-deposited weld metal amounts to approx. 25 to 35 %.
The high-strenght and ductile weld metal exhibits good
resistance to pitting, crevice corrosion and stress
corrosion cracking in chloride-bearing media. For
operating temperatures of up to +250˚C. Possible to use
equally well both with AC and DC. Fine metal droplet
transfer, good fusion of joint faces, finely rippled
bead surface, easy arc striking, restriking and slag
removal. |
|
| Materials: |
| 1.4462 |
X 2 Cr Ni Mo N 22 - 5 - 3 |
X 2 Cr Ni Mo N 22 - 5 - 3 |
- |
|
| Please observe
admissible operating temperatures for welding consumable
and base metal |
|
| All-Weld Metal Analysis (typical
values in %) : |
| 0.03 |
0.50-0.90 |
0.50-1.50 |
21.0-23.0 |
8.0-10.0 |
2.50-3.00 |
0.10-0.16 |
|
|
| Mechanical Properties of
All-Weld Metal (single values are typical values): |
|
|
| AS : As welded |
|
| Redrying: For
1 hr. at 350°C. |
|
| Welding Current [A]: |
| 40-70 |
60-90 |
90-140 |
140-210 |
|
|
| Packing & Order Information
: |
| 1098010 |
2.50 |
350 |
190 |
3.59 |
3 |
10.77 |
| 1098016 |
3.25 |
350 |
120 |
4.51 |
3 |
13.54 |
| 1098020 |
4.00 |
350 |
80 |
4.46 |
3 |
13.38 |
|
|
| Type of Current/Polarity/Welding Positions
: |